CORROSION TESTING IN ATMOSPHERES CONDUCIVE TO CORROSION

Corrosion tests aim to illustrate the effects of corrosion in nature in a short space of time. Materials or components are exposed to atmospheres conducive to corrosion in test chambers and sprayed with saline solution, for example.

Corrosion tests examine how long a component – coated or uncoated – resists corrosion. Although these tests do not illustrate the diverse climate conditions worldwide, they may nonetheless take account of important factors conducive to corrosion. These are above all high salt exposure, high moisture levels and a high temperature. A maritime climate can be especially corrosive, as high salt exposure, high moisture levels and high temperatures are combined.

In climate corrosion tests a distinction is made between constant and alternating climate conditions.

Salt spray tests are classic investigations carried out under constant conditions. These involve materials and coatings being sprayed in spraying chambers at 35 °C with a 5% salt solution, sometimes for over 1,000 hours. Sodium chloride (NaCl) is used as salt, with the pH-value at 6.5 – 7.2, relative humidity at almost 100 %. This test is also known as NSS, which stands for neutral salt spray. As a rule of thumb, 720 hours of spraying corresponds to ten years of corrosion exposure. The International Organization for Standardization (ISO) has specified regulations to be followed in these tests in its ISO 9227 standard. The full name of the standard is EN ISO 9227, Corrosion tests in artificial atmospheres — Salt spray tests.

There are different versions of salt spray tests. In acetic acid salt spray testing – ASS for short – acetic acid is added to the NaCl solution. This lowers the pH level to 3.1 to 3.3. In the copper accelerated salt spray test – CASS for short – the acetic acid NaCl solution receives the addition of copper chloride (CuCl2). This test variant is used to examine how well aluminium-oxide coats and decorative coatings consisting of copper, nickel and chrome (Cu- Ni-Cr) or nickel and chrome (Ni-Cr) protect.

Tests can be made more realistic by exposing components to multiple climates. For example, the Deutsches Institut für Bautechnik (DIBT), Berlin, employs different tests to examine the corrosion stability of surfaces. Corrosion tests in the laboratory are combined with open-air weathering in the urban climate of Berlin and on the island of Sylt.

The car industry has developed alternating climate tests for its products, which are marketed worldwide. These tests are characterised by salt spray stages with stages at higher or lower temperatures, higher and lower levels of humidity as well as alternating rest stages. These variants of salt concentration, humidity and temperature mean that the corrosion environment on the component is changing frequently. Examples: a test conducted by the German Association of the Automotive Industry (VDA) and one by the car manufacturer Volkswagen take account of frost.

In the VDA test 233-102 components are sprayed with a 1% NaCl solution for a number of hours and then exposed to temperatures of -15 to 50 °C and humidity of 50 to 95 % in other test stages. One test cycle takes a week. In the VW PV 1209 test components are sprayed with a 4 % NaCl solution and 1 % calcium chloride (CaCl2) for a number of hours and then exposed to temperatures of -40 to 80 °C and humidity of 30 to 95 % in other test stages. One test cycle also takes a week.
In two alternating climate tests of the Swedish vehicle manufacturer Volvo components are not sprayed, but sprinkled from above in stages. These tests are known as accelerated corrosion tests (ACTs).

  • In the ACT I test components are sprinkled with a 1% NaCl solution with a pH level of 4.2 for a number of hours and then exposed to temperatures of 35 to 50 °C and humidity of 40 to 95 % in other test stages. One test cycle takes a week.
  • In the ACT II test components are sprinkled with a 0.5% NaCl solution and then exposed to temperatures of 25 to 50 °C and humidity of 70 to 95 % in other test stages. One test cycle takes a week.
     

The results of the different alternating climate tests cannot be compared to one another, as the specified temperatures, humidity levels and salt content levels are too different. However, they do permit the corrosion resistance of materials or components to be compared to one another in reproducible conditions. The tests therefore show that high temperatures and condensed water accelerate corrosion.   

Misc pages

ABCDEFGHIJKLMNOPQRSTUVWXYZ
Overspray-Test
Curing
Curing in process
Conveyor belt oven (continuous oven)
Tray oven (continuos oven)
Chain conveyor oven
Chamber oven
Drying process
Cooling (after annealing)
Exhaust air treatment
KTL breakdown voltage
Condensed water test according to DIN EN ISO 6270-2
Corrosion
Sacrificial anode
Local element
Rust
Surface protection
Burnishing
Hot-dip galvanising
Flame spraying
Galvanic coating
Conversion layer
Sherardising
Substrate
Colouring
Dry-film coat thickness
Fastening properties
Gloss level
Artificial weathering test
Weathering
Test procedures
Surface properties
Chemical resistance
Mechanical resistance
Flexibility
Natural weathering test
Physical properties
Passiveness, passive state
Protection, galvanic
Protection, temporary
Scale
Chromate Coating
Passivation coating
Self-passivation
Topcoat
Rack coating
Bulk process
Partial production lot
Drum coating
Erichsen ball recess
Coating thickness, total
Coating thickness, local
Coating thickness, reference
Delamination
Coating weight
Dry to the touch
Reference surface
Ductility
Spray coating
Sealing
Electroplated coating
Specific surface
Passive corrosion protection
Inorganic protective coatings
Organic protective coatings
Active corrosion protection
Forms of corrosion
Types of corrosion
Surface corrosion
Shallow pitting corrosion
Pitting corrosion
Contact corrosion
Bimetallic corrosion
Stress corrosion cracking
Hydrogen induced cracking
ISO 9001
Dip-Draw
Electro-dip painting (ETL)
Electrostatic powder spraying (EPS)
Phosphating
ISO 14001
Trueness of gauge
Dip-Spin
Coefficient of friction
Setting behaviour
Fastening and assembly
Kesternich test
Material effectiveness
Environmental management
Quality management
EMAS
Magnetic induction measurement
Engulfing
Scaling protection
Powder coating
Coil coating
X-ray fluorescence analysis
Beta backscatter method
Mandrel bend test
Eddy current method (phase sensitive)
Eddy current method (amplitude sensitive)
Turnover
Corrosion College
Powder sintering process
Zinc flake coatings
X-Ray
Dip coating process
Stone impact test
Process stages of KTL-seperation
Adhesion
Corrosion testing atmospheres conducive corrosion
Coat thickness and coat thickness measurement
Adhesion test according to DIN EN ISO 10683
Cross-cut test for adhesion
Thread tolerance
Pressure water jetting test
Fertiliser resistance
Anodic dip coating (ADC)
Cathodic dip coating (CDC)

Technical terms can not always be avoided. As corrosion experts, we not only want to give you comprehensive advice, we are also interested in making you a corrosion expert yourself.

The variety around the topic of corrosion and corrosion protection is also in our glossary at home: explanations from A as in Adhesion to T as in Thread tolerance. Have fun clicking through!